紫外穩(wěn)定PC高透明 耐熱性好尺寸穩(wěn)定性 內(nèi)含脫模劑 易脫模HF1130R
- 起訂量 (千克)價格
- 25-500￥26 /千克
- 500-1000￥25.5 /千克
- ≥1000￥25 /千克
- 品牌：沙伯基礎
- 型號：25KG/袋
- 貨號：05131
- 發(fā)布日期： 2024-12-25
- 更新日期： 2025-09-30
產(chǎn)品詳請
| 品牌 | 沙伯基礎 |
| 貨號 | 05131 |
| 用途 | 注塑 |
| 牌號 | HF1130R |
| 型號 | HF1130R |
| 品名 | PC |
| 包裝規(guī)格 | 25KG/袋 |
| 外形尺寸 | 顆粒 |
| 生產(chǎn)企業(yè) | 沙伯基礎 |
| 是否進口 | 否 |
溫馨提示：
因橡塑行情波動太大，線上未能及時更新，更多詳情及技術請來電咨詢(微信同號）
產(chǎn)品名稱：PC
特性： 紫外線穩(wěn)定性，高透明，耐熱性好，內(nèi)含脫模劑。
商標：Lexan
包裝：25KG/包
型號：HF1130R
|
Property
|
| TYPICAL PROPERTIES (1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 50 mm/min
|
630
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
660
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
6
|
%
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
110
|
%
|
ASTM D 638
|
|
|
Tensile Modulus, 5 mm/min
|
24100
|
kgf/cm2
|
ASTM D 638
|
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
940
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
23500
|
kgf/cm2
|
ASTM D 790
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, notched, 23°C
|
65
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Tensile Impact, Type "S"
|
385
|
cm-kgf/cm2
|
ASTM D 1822
|
|
|
Instrumented Impact Energy @ peak, 23°C
|
553
|
cm-kgf
|
ASTM D 3763
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
HDT, 1.82 MPa, 6.4 mm, unannealed
|
126
|
°C
|
ASTM D 648
|
|
|
CTE, -40°C to 40°C, flow
|
7.E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, xflow
|
6.84E-05
|
1/°C
|
ASTM E 831
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gravity
|
1.2
|
-
|
ASTM D 792
|
|
|
Mold Shrinkage, flow, 3.2 mm
|
0.5 - 0.7
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 300°C/1.2 kgf
|
25
|
g/10 min
|
ASTM D 1238
|
|
|
OPTICAL
|
Value | Unit | Standard | |
|
Light Transmission
|
88
|
%
|
ASTM D 1003
|
|
|
Haze
|
1
|
%
|
ASTM D 1003
|
|
|
Processing
|
| Parameter | ||
|
Injection Molding
|
Value | Unit |
|
Drying Temperature
|
120
|
°C
|
|
Drying Time
|
3 - 4
|
hrs
|
|
Drying Time (Cumulative)
|
48
|
hrs
|
|
Maximum Moisture Content
|
0.02
|
%
|
|
Melt Temperature
|
270 - 295
|
°C
|
|
Nozzle Temperature
|
265 - 290
|
°C
|
|
Front - Zone 3 Temperature
|
270 - 295
|
°C
|
|
Middle - Zone 2 Temperature
|
260 - 280
|
°C
|
|
Rear - Zone 1 Temperature
|
250 - 270
|
°C
|
|
Mold Temperature
|
70 - 95
|
°C
|
|
Back Pressure
|
0.3 - 0.7
|
MPa
|
|
Screw Speed
|
40 - 70
|
rpm
|
|
Shot to Cylinder Size
|
40 - 60
|
%
|
|
Vent Depth
|
0.025 - 0.076
|
mm
|