- 起訂量 (千克)價(jià)格
- 25-100￥45 /千克
- 100-1000￥44 /千克
- ≥1000￥43 /千克
- 品牌：日 本三菱工程
- 貨號(hào)：05131
- 發(fā)布日期： 2022-12-02
- 更新日期： 2025-09-30
| 品牌 | 日 本三菱工程 |
| 貨號(hào) | 05131 |
| 用途 | 擠出級(jí) |
| 牌號(hào) | EKD2108U |
| 型號(hào) | EKD2108U |
| 品名 | PC |
| 外形尺寸 | 顆粒 |
| 生產(chǎn)企業(yè) | 日 本三菱工程 |
| 是否進(jìn)口 | 是 |
溫馨提示：因橡塑行情波動(dòng)太大，線上價(jià)格未能及時(shí)更新，更多詳情及技術(shù)問(wèn)題請(qǐng)來(lái)電咨詢(微信同號(hào)）
Processing/Physical Characteristics
Value
Unit
Test Standard
ISO Data
Melt volume-flow rate, MVR
5
cm3/10min
ISO 1133
Temperature
300
°C
-
Load
1.2
kg
-
Melt flow index, MFI
5
g/10min
ISO 1133
Temperature
300
°C
-
Load
1.2
kg
-
Molding shrinkage, parallel
0.6
%
ISO 294-4, 2577
Molding shrinkage, normal
0.6
%
ISO 294-4, 2577
Mechanical properties
Value
Unit
Test Standard
ISO Data
Tensile Modulus
2500
MPa
ISO 527
Yield stress
63
MPa
ISO 527
Yield strain
6
%
ISO 527
Strain at break
76
%
ISO 527
Flexural modulus, 23°C
2400
MPa
ISO 178
Flexural strength
97
MPa
ISO 178
Charpy impact strength, +23°C
N
kJ/m2
ISO 179/1eU
Charpy notched impact strength, +23°C
73
kJ/m2
ISO 179/1eA
Thermal properties
Value
Unit
Test Standard
ISO Data
Temp. of deflection under load, 1.80 MPa
125
°C
ISO 75-1/-2
Temp. of deflection under load, 0.45 MPa
136
°C
ISO 75-1/-2
Coeff. of linear therm. expansion, parallel
65
E-6/K
ISO 11359-1/-2
Coeff. of linear therm. expansion, normal
66
E-6/K
ISO 11359-1/-2
Burning behav. at thickness h
V-0
class
IEC 60695-11-10
Thickness tested
1.0
mm
-
Yellow Card available
yes
-
-
Electrical properties
Value
Unit
Test Standard
ISO Data
Volume resistivity
3E14
Ohm*m
IEC 62631-3-1
Surface resistivity
6E15
Ohm
IEC 62631-3-2
Comparative tracking index
212
-
IEC 60112
Other properties
Value
Unit
Test Standard
Water absorption
0.24
%
Sim. to ISO 62
Density
1200
kg/m3
ISO 1183
Processing Recommendation Extrusion
Value
Unit
Test Standard
Pre-drying - Temperature
120
°C
-
Pre-drying - Time
4 - 8
h
-
Mold temperature
70 - 100
°C
-
Zone 1
270 - 300
°C
-
Zone 2
270 - 300
°C
-
Zone 3
270 - 300
°C
-
Nozzle temperature
270 - 300
°C
-