高韌性玻纖尼龍 PA66加纖25%增強級 80G25HS BK117 黑色玻纖增強增韌級
- 起訂量 (千克)價格
- 25-100￥48 /千克
- 100-1000￥47 /千克
- ≥1000￥46 /千克
- 品牌：杜邦
- 貨號：05131
- 發布日期： 2022-11-28
- 更新日期： 2025-09-30
產品詳請
| 品牌 | 杜邦 |
| 貨號 | 05131 |
| 用途 | 注塑 |
| 牌號 | 80G25HS BK117 |
| 型號 | 80G25HS BK117 |
| 品名 | PA66 |
| 外形尺寸 | 顆粒 |
| 生產企業 | 杜邦 |
| 是否進口 | 是 |
溫馨提示：因橡塑行情波動太大，線上價格未能及時更新，更多詳情及技術問題請來電咨詢(微信同號）
特性：25％玻璃纖維增強，熱穩定的黑色聚酰胺66樹脂，具有出色的抗沖擊性。
用途：注塑成型，汽車，家具，家用電器。
Zytel® 80G25HS BK117 is a 25% glass fiber reinforced, toughened, heat stabilized, black polyamide 66 resin for injection molding.
| Rheological properties | dry / cond | Unit | Test Standard |
| Molding shrinkage, parallel | 0.3 / * | % | ISO 294-4, 2577 |
| Molding shrinkage, normal | 0.8 / * | % | ISO 294-4, 2577 |
| Mechanical properties | dry / cond | Unit | Test Standard |
| Tensile modulus | 7000 / 4500 | MPa | ISO 527-1/-2 |
| Stress at break | 120 / 90 | MPa | ISO 527-1/-2 |
| Strain at break | 4 / 8 | % | ISO 527-1/-2 |
| Charpy impact strength, +23°C | 80 / 80 | kJ/m2 | ISO 179/1eU |
| Charpy impact strength, -30°C | 80 / 80 | kJ/m2 | ISO 179/1eU |
| Charpy notched impact strength, +23°C | 22 / 24 | kJ/m2 | ISO 179/1eA |
| Charpy notched impact strength, -30°C | 14 / 13 | kJ/m2 | ISO 179/1eA |
| Thermal properties | dry / cond | Unit | Test Standard |
| Melting temperature, 10°C/min | 262 / * | °C | ISO 11357-1/-3 |
| Glass transition temperature, 10°C/min | 75 / * | °C | ISO 11357-1/-2 |
| Temp. of deflection under load, 1.80 MPa | 240 / * | °C | ISO 75-1/-2 |
| Temp. of deflection under load, 0.45 MPa | 258 / * | °C | ISO 75-1/-2 |
| FMVSS | B | - | ISO 3795 (FMVSS 302) |
| Electrical properties | dry / cond | Unit | Test Standard |
| Electric strength | 32 / - | kV/mm | IEC 60243-1 |
| Comparative tracking index | * / 375 | - | IEC 60112 |
| Other properties | dry / cond | Unit | Test Standard |
| Density | 1250 / - | kg/m3 | ISO 1183 |
| Rheological calculation properties | Value | Unit | Test Standard |
| Thermal conductivity of melt | 0.21 | W/(m K) | - |
| Ejection temperature | 210 | °C | - |